In situ powder X-ray diffraction study of the hydro-thermal formation of LiMn2O4 nanocrystallites

Research output: Contribution to journal/Conference contribution in journal/Contribution to newspaperJournal articleResearchpeer-review

  • Steinar Birgisson, Denmark
  • Kirsten Marie Ørnsbjerg Jensen, Department of Applied Physics and Applied Mathematics, Columbia University, New York, Denmark
  • Troels Lindahl Christiansen, Denmark
  • Jon Fold von Bülow, Haldor Topsøe A/S, Kgs. Lyngby, Denmark, Denmark
  • Bo Brummerstedt Iversen
In situ measurements of the hydrothermal formation of LiMn2O4 (LMO) nanocrystallites reveal that the reaction progresses in steps, each creating a different crystalline phase. The reaction route is summarized as KMnO4 -> disordered delta-MnO2 ->(ordered delta-MnO2)-> LiMn2O4 ->(gamma-Mn2O3)-> Mn3O4. The phase purity of LMO can be controlled by reaction time and temperature where phase pure LMO is obtained after 150-210 seconds at 220 C-circle or 45-140 seconds at 260 C-circle. It is also concluded that production of phase pure LMO by this method comes at the price of reduced reaction yield. From the observed reaction route an alternative way to control the phase purity is proposed by changing the amount of reducing agent. This hypothesis is rejected by a set of in situ measurements showing that the reaction kinetics of subsequent reaction steps hinders the formation of phase pure LMO. From the observation of unit cell changes as function of the transformation from LMO to Mn3O4 three distinct reaction parts are observed. This indicates that the reaction is a solid solid reaction with a phase boundary. The in situ measurements reveal that LMO first appears in the reaction solution as thin platelets with sizes ranging from 3-13 nm. As the reaction progresses the crystallites grow faster along the [111] direction giving rod-like shaped crystallites in the end. The LMO crystallites start off with the same shape at all temperatures investigated indicating that they form from delta-MnO2 crystallites.
Original languageEnglish
JournalDalton Transactions (Print Edition)
Volume43
Issue40
Pages (from-to)15075-15084
Number of pages10
ISSN1477-9226
DOIs
Publication statusPublished - 2014

    Research areas

  • ANATASE TIO2 NANOPARTICLES, METAL-ORGANIC FRAMEWORKS, LITHIUM-ION BATTERIES, ELECTROCHEMICAL PROPERTIES, SUPERCRITICAL FLUIDS, MAGNETIC-PROPERTIES, MANGANESE, GROWTH, CRYSTALLIZATION, SCATTERING