Hydrosilane-Modified Poly(2-Hydroxyethyl Methacrylate) Brush as a Nanoadhesive for Efficient Silicone Bonding

Research output: Contribution to journal/Conference contribution in journal/Contribution to newspaperJournal articleResearchpeer-review

DOI

Leaching of chemicals from adhesion promoters is, in particular, problematic for the food, water, pharmaceutical, and MedTech industries where any chemical contamination is unacceptable. A solution to this issue is to employ covalently attached nanoscale polymer brushes as adhesive layers for plastics. One of the industrially most relevant adhesion targets in that respect is poly(dimethylsiloxane) (PDMS), being used for many high-end applications such as catheters and breast implants. In this work, we have synthesized a novel surface-immobilized poly(2-hydroxyethyl methacrylate)-based brush adhesive containing reactive hydrosilane groups that can bond directly to PDMS. Two different medical grades of addition-cured PDMS were molded on top of titanium substrates already coated with the polymer brush. Titanium plates were used for the chemical analysis, and titanium rods were used for adhesion testing. Adhesion testing revealed a high adhesive force, in which cohesive failure was observed in the bulk PDMS. The necessity of the hydrosilane group in the polymer brush adhesive layer was demonstrated in comparative studies using similar brushes lacking this functionality.

Original languageEnglish
JournalACS Omega
Volume4
Issue7
Pages (from-to)12130-12135
Number of pages6
ISSN2470-1343
DOIs
Publication statusPublished - Jul 2019

    Research areas

  • CELL-ADHESION, ELECTRON-TRANSFER, FILMS, SURFACE, TRANSFER RADICAL POLYMERIZATION

See relations at Aarhus University Citationformats

ID: 168728815