Effect of partial substitution of Ca for Sr on crystal structure and luminescence of Ce-doped Sr 4 Al 14 O 25

Research output: Contribution to journal/Conference contribution in journal/Contribution to newspaperJournal articleResearchpeer-review

  • M. Misevicius, Vilnius University
  • ,
  • K. Jonikavicius, Vilnius University
  • ,
  • Jens-Erik Jørgensen
  • V. Balevicius, Vilnius University

Monophasic undoped and cerium-doped Sr 4 Al 14 O 25 samples with partial substitution of calcium for strontium were prepared using conventional solid-state synthesis. Structural studies revealed that substitution of strontium by calcium in Sr 4-x Ca x Al 14 O 25 up to x = 1.4 is possible without formation of additional phases and that the Sr2 site (of two possible) is more likely to be substituted by the smaller Ca ions. Photoluminescence measurements of Sr 4 Al 14 O 25 :Ce showed emission with double peak (360 and 380 nm) under 330 nm excitation wavelength. The effect of partial substitution of strontium by calcium on the luminescence of Sr 4-x Ca x Al 14 O 25 :Ce (emission, quantum yield, decay) were studied as well.

Original languageEnglish
JournalJournal of Solid State Chemistry
Volume274
IssueJune
Pages (from-to)116-123
Number of pages8
ISSN0022-4596
DOIs
Publication statusPublished - 2019

    Research areas

  • Crystal structure, Luminescence, Optical properties, Oxides, X-ray diffraction

See relations at Aarhus University Citationformats

ID: 148205174