Controlling structural and magnetic properties of SrFe12O19 nanoplatelets by synthesis route and calcination time

Jennifer Hölscher, Matilde Saura-Múzquiz, Jakob Ahlburg, Mathias Mørch, Didrik Konow Grønseth, Mogens Christensen*

*Corresponding author for this work

Research output: Contribution to journal/Conference contribution in journal/Contribution to newspaperJournal articleResearchpeer-review

76 Downloads (Pure)

Abstract

Nanocrystalline platelets of Sr hexaferrite, SrFe12O19, were prepared by four techniques (two hydrothermal and two sol-gel techniques) and calcined at 1000 °C for 1, 2, 4, 8 and 16 h. The microstructure of these samples was analyzed using Rietveld refinements of high-resolution synchrotron powder X-ray diffraction data, and the obtained results were correlated with the magnetic properties obtained from vibrating sample magnetometer measurements. The calcination treatment causes the crystallites to preferentially grow along the c-axis, leading to more isotropic crystallites. Moreover, the microstructural changes induced by calcination alter the magnetic properties, yielding a higher saturation magnetization in all samples. The attained coercivity is correlated with the crystallite size along the width of the platelets. Despite the pronounced changes of the microstructure and the magnetic properties after calcination, the calcination duration has a minor effect on the properties, i.e. in most cases the steady state is obtained after 1 h. The starting material has a profound impact on the microstructural change during calcination, despite the high calcination temperature.

Original languageEnglish
Article number474002
JournalJournal of Physics D: Applied Physics
Volume53
Issue47
Number of pages10
ISSN0022-3727
DOIs
Publication statusPublished - 2020

Keywords

  • Calcination
  • Hexaferrite
  • Magnetic properties
  • Synchrotron X-ray powder diffraction

Fingerprint

Dive into the research topics of 'Controlling structural and magnetic properties of SrFe12O19 nanoplatelets by synthesis route and calcination time'. Together they form a unique fingerprint.

Cite this