Operando X-ray scattering study of thermoelectric β-Zn4Sb3

Research output: Contribution to journal/Conference contribution in journal/Contribution to newspaperJournal articleResearchpeer-review

The application of thermoelectrics for energy harvesting depends strongly on operational reliability and it is therefore desirable to investigate the structural integrity of materials under operating conditions. We have developed an operando setup capable of simultaneously measuring X-ray scattering data and electrical resistance on pellets subjected to electrical current. Here, operando investigations of β-Zn4Sb3 are reported at current densities of 0.5, 1.14 and 2.3 A mm-2. At 0.5 A mm-2 no sample decomposition is observed, but Rietveld refinements reveal increased zinc occupancy from the anode to the cathode demonstrating zinc migration under applied current. At 1.14 A mm-2 β-Zn4Sb3 decomposes into ZnSb, but pair distribution function analysis shows that Zn2Sb2 units are preserved during the decomposition. This identifies the mobile zinc in β-Zn4Sb3 as the linkers between the Zn2Sb2 units. At 2.3 A mm-2 severe Joule heating triggers transition into the γ-Zn4Sb3 phase, which eventually decomposes into ZnSb, demonstrating Zn ion mobility also in γ-Zn4Sb3 under electrical current.

Original languageEnglish
JournalIUCrJ
Volume7
IssuePart 1
Pages (from-to)100-104
Number of pages5
ISSN2052-2525
DOIs
Publication statusPublished - Jan 2020

    Research areas

  • electrical resistance, operando study, pair distribution function, powder X-ray diffraction, thermoelectric materials, zinc antimonides

See relations at Aarhus University Citationformats

ID: 185268605