Zinc antimonide thin film based flexible thermoelectric module

Publikation: Bidrag til tidsskrift/Konferencebidrag i tidsskrift /Bidrag til avisTidsskriftartikelForskningpeer review

  • Seyedmohammad Mortazavinatanzi, Aalborg Universitet
  • ,
  • Mojtaba Mirhosseini, Aalborg Universitet
  • ,
  • Lirong Song
  • Bo Brummerstedt Iversen
  • Lasse Rosendahl, Aalborg Universitet
  • ,
  • Alireza Rezania, Aalborg Universitet

Zinc-antimonide is an encouraging alternative thermoelectric material to bismuth telluride based material for medium temperature range applications. In this work two fabrication concepts are proposed to build flexible modules using P-type zinc-antimony thin film and constantan straps, where the constantan was used as flexible electrical interconnect and N-type thermoelectric element. Nano-silver paste was applied as the bonding material and adhesive substance to tolerate a higher range of temperatures. The thin film specimen consisted of a 600 nm thin layer of zinc-antimonide deposited by magnetron co-sputtering on a 350 µm thick glass substrate. The proposed device configurations generate peak power of 3.5 μW and 13.5 μW at hot side temperatures of 250 °C and 330 °C, respectively.

OriginalsprogEngelsk
Artikelnummer128582
TidsskriftMaterials Letters
Vol/bind280
ISSN0167-577X
DOI
StatusUdgivet - dec. 2020

Se relationer på Aarhus Universitet Citationsformater

ID: 196174605