Synthesis, structure and NH3 sorption properties of mixed Mg1-xMnx(NH3)6Cl2 ammines

Publikation: Bidrag til tidsskrift/Konferencebidrag i tidsskrift /Bidrag til avisTidsskriftartikelForskningpeer review


  • Perizat Berdiyeva, Institute for Energy Technology
  • ,
  • Anastasiia Karabanova, Danmarks Tekniske Universitet
  • ,
  • Jakob B. Grinderslev
  • Rune E. Johnsen, Danmarks Tekniske Universitet
  • ,
  • Didier Blanchard, Danmarks Tekniske Universitet
  • ,
  • Bjørn C. Hauback, Institute for Energy Technology
  • ,
  • Stefano Deledda, Institute for Energy Technology

This paper describes the synthesis, crystal structure, and NH3 sorption properties of Mg1- xMnx(NH3)6Cl2 (x = 0-1) mixed metal halide ammines, with reversible NH3 storage capacity in the temperature range 20-350 °C. The stoichiometry (x) dependent NH3 desorption temperatures were monitored using in situ synchrotron radiation powder X-ray diffraction, thermogravimetric analysis, and differential scanning calorimetry. The thermal analyses reveal that the NH3 release temperatures decrease in the mixed metal halide ammines in comparison to pure Mg(NH3)6Cl2, approaching the values of Mn(NH3)6Cl2. Desorption occurs in three steps of four, one and one NH3 moles, with the corresponding activation energies of 54.8 kJ∙mol-1, 73.2 kJ∙mol-1 and 91.0 kJ∙mol-1 in Mg0.5Mn0.5(NH3)6Cl2, which is significantly lower than the NH3 release activation energies of Mg(NH3)6Cl2 (Ea = 60.8 kJ∙mol-1, 74.8 kJ∙mol-1 and 91.8 kJ∙mol-1). This work shows that Mg1- xMnx(NH3)yCl2 (x = 0 to 1, y = 0 to 6) is stable within the investigated temperature range (20-350 °C) and also upon NH3 cycling.