Optimizing the energy product of exchange-coupled soft/hard Zn0.2Fe2.8O4/SrFe12O19magnets

Publikation: Bidrag til tidsskrift/Konferencebidrag i tidsskrift /Bidrag til avisTidsskriftartikelForskningpeer review

DOI

Permanent magnets based on ferrites are currently studied as possible alternatives, in several application areas, to rare-earth-based magnets to overcome the barriers of high costs, unavailability, and environmental impact. Their attractiveness lies in the large crystalline anisotropy, ensuring resistance to demagnetization, and the possibility of having their modest saturation magnetization enhanced through exchange-coupling with a compatible soft magnetic material of higher saturation magnetization. Using analytical calculations, a micromagnetic finite element model, and comparison with measurements on a produced sample, the conditions that give the highest possible maximum energy product are determined for ferrite-based exchange-coupled Zn0.2Fe2.8O4/SrFe12O19 soft/hard nanocomposite magnets. Two geometries are considered: A spherical core-shell geometry and a composite granular microstructure. Two sets of material parameters are considered for the granular structure, one from the literature and one obtained by fitting to the measured magnetization data. The results show that it is important to have a well-aligned easy axis of hard grains and that the optimal amount of the soft material depends on the alignment of the hard grains as well as their size, with smaller grains yielding larger (BH)max values. The core-shell model shows that the maximum (BH)max can be strongly enhanced, from ∼40 to ∼60 kJ/m3, by using a hard core diameter of <30 nm and a soft shell thickness of <7 nm. The composite granular structure yields a maximum (BH)max of ∼50 kJ/m3 for a soft volume fraction of 43%.

OriginalsprogEngelsk
Artikelnummer163904
TidsskriftJournal of Applied Physics
Vol/bind132
Nummer16
Antal sider11
ISSN0021-8979
DOI
StatusUdgivet - okt. 2022

Bibliografisk note

Publisher Copyright:
© 2022 Author(s).

Se relationer på Aarhus Universitet Citationsformater

ID: 292716459