On the enhanced phosphorus doping of nanotextured black silicon

Giuseppe Scardera, Shaozhou Wang, Yu Zhang, Muhammad Umair Khan, Shuai Zou, Daqi Zhang, Rasmus Schmidt Davidsen, Ole Hansen, Ly Mai, David N.R. Payne, Bram Hoex, Malcolm D Abbott

Publikation: Bidrag til tidsskrift/Konferencebidrag i tidsskrift /Bidrag til avisTidsskriftartikelForskningpeer review

25 Downloads (Pure)

Abstract

The integration of nanotextured black silicon (B-Si) into solar cells is often complicated by its enhanced phosphorus doping effect, which is typically attributed to increased surface area. In this article, we show that B-Si's surface-to-volume ratio, or specific surface area (SSA), which is directly related to surface reactivity, is a better indicator of reduced sheet resistance. We investigate six B-Si conditions with varying dimensions based on two morphology types prepared using metal-catalyzed chemical etching and reactive-ion etching. We demonstrate that for a POCl3 diffusion, B-Si sheet resistance decreases with increasing SSA, regardless of surface area. 2-D dopant contrast imaging of different textures with similar surface areas also indicates that the extent of doping is enhanced with increasing SSA. 3-D diffusion simulations of nanocones show that both the extent of radial doping within a texture feature and the metallurgical junction depth in the underlying substrate increase with increasing SSA. We suggest SSA should be considered more readily when studying B-Si and its integration into solar cells.

OriginalsprogEngelsk
Artikelnummer9328858
TidsskriftIEEE Journal of Photovoltaics
Vol/bind11
Nummer2
Sider (fra-til)298-305
Antal sider8
ISSN2156-3381
DOI
StatusUdgivet - mar. 2021
Udgivet eksterntJa

Fingeraftryk

Dyk ned i forskningsemnerne om 'On the enhanced phosphorus doping of nanotextured black silicon'. Sammen danner de et unikt fingeraftryk.

Citationsformater