Impact of PEG Chain Length on the Physical Properties and Bioactivity of PEGylated Chitosan/siRNA Nanoparticles in Vitro and in Vivo

Publikation: Bidrag til tidsskrift/Konferencebidrag i tidsskrift /Bidrag til avisTidsskriftartikelForskningpeer review


  • Chuanxu Yang
  • ,
  • Shan Gao, Suzhou Ribo Life Science Co., Ltd. , Beijing, China.
  • ,
  • Frederik Dagnæs-Hansen
  • ,
  • Maria Jakobsen
  • ,
  • Jørgen Kjems

PEGylation of cationic polyplexes is a promising approach to enhance the stability and reduce unspecific interaction with biological components. Herein, we systematically investigate the impact of PEGylation on physical and biological properties of chitosan/siRNA polyplexes. A series of chitosan-PEG copolymers (CS-PEG2k, CS-PEG5k and CS-PEG10k) were synthesized with similar PEG mass content but with different molecular weight. PEGylation with higher molecular weight and less grafting degree resulted in smaller and more compacted nanoparticles with relatively higher surface charge. PEGylated polyplexes showed distinct mechanism of endocytosis, which was macropinocytosis and caveolae-dependent and clathrin-independent. In vitro silencing efficiency in HeLa and H1299 cells was significantly improved by PEGylation and CS-PEG5k/siRNA achieved the highest knockdown efficiency. Efficient silence of ribonucleotide reductase subunit M2 (RRM2) in HeLa cells by CS-PEG5k/siRRM2 significantly induced cell cycle arrest and inhibited cell proliferation. In addition, PEGylation significantly inhibited macrophage phagocytosis and unspecific interaction with red blood cells (RBCs). Significant extension of in vivo circulation was achieved only with high molecular weight PEG modification (CS-PEG10k), whereas all CS/siRNA and CS-PEG/siRNA nanoparticles showed similar pattern of biodistribution with major accumulation in liver and kidney. These results imply that PEGylation with higher molecular weight PEG and less grafting rate is a promising strategy to improve chitosan/siRNA nanocomplexes performance both in vitro and in vivo.

TidsskriftA C S Applied Materials and Interfaces
Sider (fra-til)12203-12216
StatusUdgivet - 12 apr. 2017

Se relationer på Aarhus Universitet Citationsformater

ID: 111661866