Effect of grain boundary on the crack-tip plasticity under hydrogen environment: An atomistic study

Publikation: Bidrag til tidsskrift/Konferencebidrag i tidsskrift /Bidrag til avisTidsskriftartikelForskningpeer review

DOI

  • Kai Zhao, Norwegian University of Science and Technology
  • ,
  • Jianying He, Norges teknisk-naturvitenskapelige universitet, Trondheim
  • ,
  • Zhiliang Zhang, Norges teknisk-naturvitenskapelige universitet, Trondheim

It has been found that the plasticity is significantly affected by the hydrogen interstitials in metallic materials. However, the underlying physics responsible for the dislocation/hydrogen interactions is still poorly understood. Using molecular dynamics simulations, we study the emission of dislocations from a crack tip in fcc Ni single-crystal and bicrystal samples under a hydrogen environment. The results show that the critical mode-I stress intensity factor (SIF) is reduced due to the presence of hydrogen, but the existence of ς5 grain boundaries (GBs, with an inclination angle ranging from 0 to π/4) almost does not alter the critical mode-I SIF for dislocation emission, compared with the single-crystal cases. These findings suggest that further large-scale investigations should be conducted to study the influence of various microstructural factors, such as the distance from the crack tip to GB and density of GB as well as the existence of other defects, e.g., voids and inclusions.

OriginalsprogEngelsk
Artikelnummer015101
TidsskriftJournal of Applied Physics
Vol/bind127
Nummer1
Antal sider9
ISSN0021-8979
DOI
StatusUdgivet - 2020

Se relationer på Aarhus Universitet Citationsformater

ID: 183249768