A universal approach for the synthesis of two-dimensional binary compounds

Publikation: Bidrag til tidsskrift/Konferencebidrag i tidsskrift /Bidrag til avisTidsskriftartikelForskningpeer review

DOI

  • Abhay Shivayogimath, Technical University of Denmark
  • ,
  • Joachim Dahl Thomsen, Technical University of Denmark
  • ,
  • David M.A. Mackenzie, Technical University of Denmark, Aalto University
  • ,
  • Mathias Geisler, Technical University of Denmark
  • ,
  • Raluca Maria Stan
  • ,
  • Ann Julie Holt
  • Marco Bianchi
  • Andrea Crovetto, Technical University of Denmark
  • ,
  • Patrick R. Whelan, Technical University of Denmark
  • ,
  • Alexandra Carvalho, National University of Singapore
  • ,
  • Antonio H.Castro Neto, National University of Singapore
  • ,
  • Philip Hofmann
  • Nicolas Stenger, Technical University of Denmark
  • ,
  • Peter Bøggild, Technical University of Denmark
  • ,
  • Timothy J. Booth, Technical University of Denmark

Only a few of the vast range of potential two-dimensional materials (2D) have been isolated or synthesised to date. Typically, 2D materials are discovered by mechanically exfoliating naturally occurring bulk crystals to produce atomically thin layers, after which a material-specific vapour synthesis method must be developed to grow interesting candidates in a scalable manner. Here we show a general approach for synthesising thin layers of two-dimensional binary compounds. We apply the method to obtain high quality, epitaxial MoS2 films, and extend the principle to the synthesis of a wide range of other materials—both well-known and never-before isolated—including transition metal sulphides, selenides, tellurides, and nitrides. This approach greatly simplifies the synthesis of currently known materials, and provides a general framework for synthesising both predicted and unexpected new 2D compounds.

OriginalsprogEngelsk
Artikelnummer2957
TidsskriftNature Communications
Vol/bind10
Nummer1
ISSN2041-1723
DOI
StatusUdgivet - 2019