Synthesis and characterization of conventional and mesoporous Ga-MFI for ethane dehydrogenation

Research output: Research - peer-reviewJournal article

  • Karen Thrane Leth
    Karen Thrane LethTechnical University of DenmarkDenmark
  • Anne Krogh Rovik
    Anne Krogh RovikTechnical University of DenmarkDenmark
  • Martin Spangsberg Holm
    Martin Spangsberg HolmTechnical University of DenmarkDenmark
  • Michael Brorson
    Michael BrorsonHaldor Topsøe A/SDenmark
  • Hans Jørgen Jakobsen
  • Jørgen Skibsted
  • Claus Hviid Christensen
    Claus Hviid ChristensenHaldor Topsøe A/SDenmark
  • Interdisciplinary Nanoscience Center
  • Department of Chemistry
 

Gallium was for the first time incorporated into the crystal structure of a mesoporous MFI zeolite. As a reference material, a well defined conventional MFI zeolite with gallium incorporated was also synthesized. The materials were characterized by XRPD, NH3-TPD, elemental analysis, N2 physisorption measurements, SEM, FT-IR as well as 29Si and 71Ga MAS NMR spectroscopy. The Ga contents correspond to molar ratios of Si/Ga= 43 and Si/Ga= 38 for the conventional and mesoporous Ga-MFI, respectively. The different types of analysis show that two almost identical zeolites were synthesized, the main difference being the morphology of the crystals. The catalytic properties of the samples were tested in ethane dehydrogenation at 823 K and at atmospheric pressure. The two Ga-MFI samples differ greatly in conversion of ethane, as a result of their difference in porosity, and it is found that the conversion is significantly improved by introducing mesopores into the structure. The major product is ethene for the conventional Ga-MFI, but there are significant amount of benzene and toluene by products for the mesoporous Ga-MFI. The 71Ga isotropic chemical shift and second-order quadrupolar effect parameter is reported for tetrahedral Ga incorporated in the MFI structure and it is shown that absorbed water molecules have an important impact on the 71Ga electric field gradients and thereby on the quantitative evaluation of the 71Ga MAS NMR intensities.

Original languageEnglish
JournalApplied Catalysis A: General
Volume348
Pages (from-to)257-265
Number of pages9
ISSN0926-860X
StatePublished - 2008

See relations at Aarhus University Citationformats

ID: 12739866